Product Description

Product Description

Tunsgten cemented carbide strips is mainly made of WC （tungsten carbide） and Co （cobalt ）mixed by metallurgical method through powder making, ball milling, pressing and sintering, the main alloy composition is WC and Co, the composition content of WC and Co in cemented carbide strips for different applications is not the same, the use range is extremely wide.

BRAND,PERFORMANCE AND APPLICATION

Grade	ISO	Density	Hardnes	T.R.S	Performance & application recommended
Grade	ISO	g/cm³	HRA	MPa	Performance & application recommended
YG6	K10	14.90	90.5	2400	Good wear resistance, suitable for machining hard wood, raw wood, aluminum section bar, brass rod and cast iron.
YG6A	K10	14.85	92.5	2000	Wear resistance higher than YG6, suitable for machining hard wood, raw wood, aluminum section bar, brass rod and cast iron.
YG8	K20	14.70	89.8	2800	High wear and impact resistance，suitable for machining dry wood, soft wood and non-ferrous metal section bar.
YS2T	K30	14.25	92	2400	Fine grain alloy, with high wear resistance, bending strength,bonding resistance and thermal strength. It is suitable for machining refractory alloys, stainless steel, high manganese steel, etc.
YL10.2	K30	14.45	91.8	3000	Wear resistance and strength comparatively higher,suitable for machining cast iron,non-ferrous metal and non-metallid materials.

Size Specification for Tungsten Carbide Strips

H903ef3681e084cb79d5d2dedb07853ede

If you need tungsten carbide strips, please advise the length, width and thickness.

Application scope of cemented carbide long bar

Cemented carbide long bar has the characteristics of high red hardness, good weldability, high hardness, high wear resistance, mainly used in the production and processing of solid wood, density board, gray cast iron, non-ferrous metal materials, chilled cast iron, hardened steel, PCB, brake materials. The use should be specifically based on the use of the selection of the appropriate material carbide long bar.